阜阳内缝补焊机 优质高效无变形焊机

  内缝埋弧补焊机

该设备**于电力钢杆、通信钢杆、高杆灯杆体套接部位内焊缝的补焊。可使钢管杆的杆体套接部位的纵焊缝达到**的焊透，焊接质量达到一级，焊缝成形美观。该设备使用灵活、方便、可靠。焊接电源为美国林肯电源。

                                  Internal seam submerged arc welding machine   

The equipment is specially used for the welding of the welding seam in the socket part of the power steel rod, the communication steel rod and the high pole lamp rod body. It can make the longitudinal weld of the steel rod to reach ** penetration, the welding quality reaches the first grade, and the weld is beautiful. The equipment is flexible, convenient and reliable. Welding power source for the United States Lincoln power supply.

联系方式: 

上海佳惠机械设备有限公司

许经理:

吴经理：

地址:上海市奉贤区奉城镇川南奉公路8739号

网址： 

Contact information:  

Shanghai Jiahui Machinery equipment Co., Ltd.

Address: No. 8739, south Sichuan road, Fengcheng, Fengxian district, shanghai

 Web site:     

常见焊缝缺陷的修补方法

一，概述

在压力容器、压力管道、船舰、钢结构等生产制造安装中免不了出现焊缝缺陷，如何消除缺陷，即如何快速、高质量完成有缺陷焊缝的返修是关系到生产单位产品质量和企业信誉，必须高度重视。目前，产品焊接的方法普遍使用手工钨极氩弧焊、CO2气体保护焊、焊条电弧焊、埋弧焊、熔化较气体保护焊等，而对焊缝缺陷返修一般采用焊条电弧焊或手工钨极氩弧焊。因为这两种焊接方法虽然焊接速度慢，却焊缝的质量高，但必须由焊接技能高的焊工担任，才能出色完成返修任务，还必须掌握一些返修知识。

二，焊前准备

1，任何需要返修焊补的地方，首先清理干净，包括附近区域；将受热有影响的零件（如橡胶件、塑料件等）拆下。

2，根据焊接检验结果，确定返修部位，采取适当的方法（常用刨削、磨削等）去除缺陷，注意每次刨削不要太厚，通常2～3mm，以便及时发现缺陷。

3，刨削后，必须打磨氧化皮、渗碳层、残渣等，露出金属光泽，坡口底应显U形，不能有沟槽等死角。对于裂纹、气孔等缺陷，常用磁粉或着色检查并确认已全部清除干净。

4，焊材的选择，焊材采购必须有出厂合格证，返修补焊时所选焊条（焊丝）不宜太粗，焊条≤3.2mm,焊丝≤2.0mm,焊材要按规定进行严格烘干处理，放入保温筒内，随用随取；严格管理制度，同批焊条不得连续烘干两次。在特殊天气（如冬天），要做好保温措施。